Super quality Mosi2 heating elements - w type Specificaton & Trade Terms
Model | w type |
---|
Place Of Origin | China |
---|
Packaging | first step, packed with sponge and box case, and then put it into wooden case |
---|
Brand | Yuhao |
---|
Certifications | ISO9001 |
---|
Price Term | EX-Work |
---|
Payment Term | T/T |
---|
Supply Ability | 5000 pieces per month |
---|
Minimum Order | 6 pieces |
---|
Loading Ports | Qingdao,Tianjin,Shanghai |
---|
Delivery Time | 7-15 days |
---|
Briefly description
Molybdenum disilicide (MoSi2) heating elementis a resistance generate-heating component made from MoSi2 or the basic material. It is used in high temperature under the oxidizing atmosphere, it looks like glass in its surface and form a light SiO2 glass film which can protect the element not to be oxidized. So this kind of element has unique effect for resisting oxidization in the high temperature. It is used to the highest temperature up to 1800C during oxidizing atmosphere. According to your request, our company can produce the products of Pole, "U", "W" and "U"-right angle shapes, etc.
MoSi2 heating element can usually make use of furnace temperature from 1300C to 1800C. It is extensively used in the industries of metallurgy, glass, ceramic refractory, crystal electronic device, industrial furnace manufacture, etc.. It is an essential ideal element when the products are sintering in the high temperature.
MoSi2 heating elements physics and chemistry characters:
1. Physics Characters
Volume Density Bending Strength Vickers Hardness Porosity Water absorption Heating Elongation Rate
5.5 g/cm3 15-25 kg/cm3 (HV)570kg/mm2 7.4% 1.2% 4%
2. Chemistry Character MoSi2 heating element is used in the high temperature under oxidizing atmosphere. It will form the SiO2 film which can keep the element from being melted. During the oxidizing process, the SiO2 protecting film is formed again when the element continues to be used. The MoSi2 heating element must not be used in the temperature between 400C and 700C for a long time, otherwise the element will be cremated under the strong oxidizing function in the low temperature.